High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - A4009MFN1325
| Melt flow rate, (2.16 kg), g/10min | 0.7-1,1 |
| Density kg/m3 | 958-962 |
| Tensile yield strength, at 50 mm/min, Mpa | 27 |
| Tensile elongation at yield, at 50 mm/min, Mpa | 19 |
| Elongation at break % | 500 |
| Flexural modulus (1% secant), at 1.4mm/min, Mpa | 1000 |
High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - B50-35H-111
| Melt flow rate, (2.16 kg) g/10min | 0,3-0,4 |
| Density kg/m3 | 948-952 |
| Tensile yield strength, at 2 inch/min, Mpa | 21 |
| Tensile elongation at yield, % | 500 |
| Flexural modulus (1% secant), at 1.4 mm/min, Mpa | 900 |
| Heat resisitance on Vicat , °С | 120 |
| Bell Telephone thermal testing on the breakdown voltage , resistance to cracking when the voltage, at 50 °С |
30 h |
High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - НР50-25-155
| Melt flow rate, (2.16 kg), g/10min | 0,18-0,26 |
| Density, kg/m3 | 949-953 |
| Tensile yield strength, (2 inch/min), Mpa | 22 |
| Tensile elongation at yield, % | 700 |
| Heat resistance on Vicat , Mpa | 120 |
| Flexural modulus, Mpa | 900 |
High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - INpipe 100
| Melt flow rate, (2.16 kg), g/10min | 0,25-0,35 |
| Density, kg/m3 | 957-961 |
| Tensile yield strength, at 2 inch/min, Mpa | 21 |
| Tensile elongation at yield, % | 600 |
| Heat resisitance on Vicat, °С | 120 |
| Bell Telephone thermal testing on the breakdown voltage , resistance to cracking when the voltage, at 50 °С |
1000 h |
High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - J53-08 N2000
| Melt flow rate, (21.6 kg), g/10min | 6,5-9,5 |
| Density 23 °С, kg/m3 | 951-955 |
| Tensile strength at yield longitudinal direction, Mpa | 27 |
| Tensile strength at yield in transverse direction, Mpa | 25 |
| Tensile strength at break in the longitudinal direction, Mpa | 66 |
| Tensile at break in the longitudinal tranverse direction, % | 250 / 350 |
| Impact strength, g/10 min | 250 |
High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - Т50-500
| Melt flow rate, (2.16 kg) , g/10min | 5,4-7,6 |
| Density, kg/m3 | 951-955 |
| Tensile yield strength, Mpa | 24 |
| Tensile elongation at yield, % | 800 |
| Flexural modulus (1 mm/min), Mpa | 900 |
| Notched izod under load, J/m | 57 |
| Heat resisitance on Vicat, °С | 120 |
High-Density Polyethylene Specification (granulated)
TDS (State Turkmenistan Standart Service)-1097-2018
Mark - Т60-475-119
| Melt flow rate, (2.16 kg) , g/10min | 4 -5,6 |
| Density, kg/m3 | 959-963 |
| Tensile yield strength, Mpa | 28 |
| Notched izod under load, J/m | 55 |
| Flexural modulus (1 mm/min), Mpa | 1250 |
| Heat resisitance on Vicat | 120 °С |