Polypropylene L R7175-35.P Random Copolymer

TDS (State Turkmenistan Standart Service)-1097-2018

Melt flow rate, (230°С / 2.16 g), g/10min	35
Density g/cm3	0.902
Tensile yield strength, at 50 mm/min, Mpa	28
Tensile elongation at yield, at 50 mm/min, %	8.00
Notched Izod impact strength, at 23°С, J/m	38
Flexural modulus (1% secant), at 1.3mm/min, Mpa	1100

Polypropylene L H5088-25G.O Homopolymer

TDS (State Turkmenistan Standart Service)-1097-2018

Melt flow rate, (230°С / 2.16 g), g/10min	25
Density g/cm3	0.902
Tensile yield strength, at 50 mm/min, Mpa	35
Tensile elongation at yield, at 50 mm/min, %	7.00
Notched Izod impact strength, at 23°С, J/m	24
Flexural modulus (1% secant), at 1.3mm/min, Mpa	1480

Polypropylene L H5072-03.O Homopolymer

TDS (State Turkmenistan Standart Service)-1097-2018

Melt flow rate, (230°С / 2.16 g), g/10min	3.5
Density g/cm3	0.902
Tensile yield strength, at 50 mm/min, Mpa	35
Tensile elongation at yield, at 50 mm/min, %	8.00
Notched Izod impact strength, at 23°С, J/m	40
Flexural modulus (1% secant), at 1.3mm/min, Mpa	1500

Polypropylene L H3066-03.O Homopolymer

TDS (State Turkmenistan Standart Service)-1097-2018

Melt flow rate, (230°С / 2.16 g), g/10min	3.4
Density g/cm3	0.902
Tensile yield strength, at 50 mm/min, Mpa	32
Tensile elongation at yield, at 50 mm/min, %	9.00
Notched Izod impact strength, at 23°С, J/m	50
Flexural modulus (1% secant), at 1.3mm/min, Mpa	1400

Polypropylene L H3150-02.O Homopolymer

TDS (State Turkmenistan Standart Service)-1097-2018

Melt flow rate, (230°С / 2.16 g), g/10min	2.5
Density g/cm3	0.902
Tensile yield strength, at 50 mm/min, Mpa	35
Tensile elongation at yield, at 50 mm/min, %	8.00
Notched Izod impact strength, at 23°С, J/m	45
Flexural modulus (1% secant), at 1.3mm/min, Mpa	1600